Preparation of bromine intercalated pyrolytic carbon

Jin Hua Lu; He Jun Li; Ke Zhi Li

Preparation of bromine intercalated pyrolytic carbon

Jin Hua Lu
, He Jun Li
, Ke Zhi Li

材料学院

Northwestern Polytechnical University Xian

科研成果: 期刊稿件 › 文章 › 同行评审

摘要

Pyrolytic carbon prepared by chemical vapor deposition was intercalated by bromine in the liquid phase at 20 °C for 48 h with a weight ratio of bromine to carbon of 6. XRD, SEM and XPS were used to characterize the product. Results show that a new XRD diffraction peak appears after intercalation. XPS further shows that the bromine and carbon are chemically bonded.

源语言	英语
页（从-至）	185-188
页数	4
期刊	Xinxing Tan Cailiao/New Carbon Materials
卷	23
期	2
出版状态	已出版 - 6月 2008

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{4e2bc325061740adbc5d4a224906f038,

title = "Preparation of bromine intercalated pyrolytic carbon",

abstract = "Pyrolytic carbon prepared by chemical vapor deposition was intercalated by bromine in the liquid phase at 20 °C for 48 h with a weight ratio of bromine to carbon of 6. XRD, SEM and XPS were used to characterize the product. Results show that a new XRD diffraction peak appears after intercalation. XPS further shows that the bromine and carbon are chemically bonded.",

keywords = "Bromine, Carbon/carbon composite, Intercalation, Pyrolytic carbon",

author = "Lu, \{Jin Hua\} and Li, \{He Jun\} and Li, \{Ke Zhi\}",

year = "2008",

month = jun,

language = "英语",

volume = "23",

pages = "185--188",

journal = "Xinxing Tan Cailiao/New Carbon Materials",

issn = "2097-1605",

publisher = "Science Press ",

number = "2",

}

TY - JOUR

T1 - Preparation of bromine intercalated pyrolytic carbon

AU - Lu, Jin Hua

AU - Li, He Jun

AU - Li, Ke Zhi

PY - 2008/6

Y1 - 2008/6

N2 - Pyrolytic carbon prepared by chemical vapor deposition was intercalated by bromine in the liquid phase at 20 °C for 48 h with a weight ratio of bromine to carbon of 6. XRD, SEM and XPS were used to characterize the product. Results show that a new XRD diffraction peak appears after intercalation. XPS further shows that the bromine and carbon are chemically bonded.

AB - Pyrolytic carbon prepared by chemical vapor deposition was intercalated by bromine in the liquid phase at 20 °C for 48 h with a weight ratio of bromine to carbon of 6. XRD, SEM and XPS were used to characterize the product. Results show that a new XRD diffraction peak appears after intercalation. XPS further shows that the bromine and carbon are chemically bonded.

KW - Bromine

KW - Carbon/carbon composite

KW - Intercalation

KW - Pyrolytic carbon

UR - https://www.scopus.com/pages/publications/53649099506

M3 - 文章

AN - SCOPUS:53649099506

SN - 2097-1605

VL - 23

SP - 185

EP - 188

JO - Xinxing Tan Cailiao/New Carbon Materials

JF - Xinxing Tan Cailiao/New Carbon Materials

IS - 2

ER -

Preparation of bromine intercalated pyrolytic carbon

摘要

其它文件与链接

指纹

引用此