Pre-processing related recrystallization behavior in β annealing of a near-β Ti-5Al-5Mo-5V-3Cr-1Zr titanium alloy

Recrystallization behavior of Ti-55531 alloy in β annealing is explored for grain refinement during primary hot working. Four typical pre-processing conditions were adopted to characterize the diverse processing routes of primary hot working: deformation and annealing in the two-phase region, deformation of globularized structure in two-phase region, deformation of lamellar structure in two-phase region and deformation in single β region. The microstructure evolution in β annealing was quantified by Optical Microscopy (OM), Electron Backscattered Diffraction (EBSD), X-ray diffraction (XRD) and quantitative metallography. The results indicate that the nucleation mode of static recrystallization is determined by the size and distribution of substructures prior to annealing which is related to pre-processing route. The uniform substructures in as-deformed globularized structure produce a higher fraction of low angle grain boundaries after full recrystallization. Fine β recrystallized structure can be obtained when β recrystallization is accompanied by α-to-β phase transformation.