Microstructure evolution and nitrides precipitation in in-situ Ti ₂AlN/TiAl composites during isothermal aging at 900 °c

Microstructures of Ti₂AlN/TiAl composites prepared by in-situ method were characterized in in-situ and aging treatment conditions and the nitride precipitation was investigated in Ti₂AlN/TiAl composites aged at 900 °C for 24 h after being heat treated at 1400 °C for 0.5 h. The in-situ composites consist of γ+α₂ lamellar colonies, equiaxed γ grains and Ti₂AlN reinforcements. Matrix with nearly fully lamellar structure formed after solution and subsequently aging treatment. With the increase of Ti₂AlN content, the nearly fully lamellar structure becomes instable for the aged composites. According to TEM study, fine Ti₂AlN precipitates are found to distribute at the grain boundaries of lamellar colony. Needle-like Ti₃AlN precipitates arrange in line with growing axis parallel to [001] direction of the γ-TiAl matrix and another needle-like Ti₃AlN precipitates with lager size distribute at the dislocations.