Microstructure and oxidation resistance of Si-Mo-B coating for C/SiC coated carbon/carbon composites

Yu Lei Zhang; He Jun Li; Zhi Xiong Hu; Jin Cui Ren; Ke Zhi Li

doi:10.1016/j.corsci.2013.03.015

Microstructure and oxidation resistance of Si-Mo-B coating for C/SiC coated carbon/carbon composites

Yu Lei Zhang
, He Jun Li
, Zhi Xiong Hu
, Jin Cui Ren
, Ke Zhi Li

材料学院

Northwestern Polytechnical University Xian

科研成果: 期刊稿件 › 文章 › 同行评审

65 引用（Scopus）

摘要

A self-sealing Si-Mo-B oxidation resistance coating was prepared on C/SiC coated carbon/carbon (C/C) composites by slurry and high temperature treatment method. The oxidation resistance of the coating increases at 1173. K and first increases then decreases at 1873. K with the increase of B content from 0 to 20. wt.%. The C/SiC/gradient Si-Mo-B multilayer coating can protect C/C composite from oxidation for 100. h at 1173. K and 125. h at 1873. K. The good oxidation resistance of the coating in broad temperature range could be attributed to its good self-sealing property.

源语言	英语
页（从-至）	150-155
页数	6
期刊	Corrosion Science
卷	72
DOI	https://doi.org/10.1016/j.corsci.2013.03.015
出版状态	已出版 - 7月 2013

访问文件

10.1016/j.corsci.2013.03.015

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{63b945e21d034048bff2f9139ee25137,

title = "Microstructure and oxidation resistance of Si-Mo-B coating for C/SiC coated carbon/carbon composites",

abstract = "A self-sealing Si-Mo-B oxidation resistance coating was prepared on C/SiC coated carbon/carbon (C/C) composites by slurry and high temperature treatment method. The oxidation resistance of the coating increases at 1173. K and first increases then decreases at 1873. K with the increase of B content from 0 to 20. wt.\%. The C/SiC/gradient Si-Mo-B multilayer coating can protect C/C composite from oxidation for 100. h at 1173. K and 125. h at 1873. K. The good oxidation resistance of the coating in broad temperature range could be attributed to its good self-sealing property.",

keywords = "A. Ceramic matrix composites, B. Weight loss, C. Oxidation",

author = "Zhang, \{Yu Lei\} and Li, \{He Jun\} and Hu, \{Zhi Xiong\} and Ren, \{Jin Cui\} and Li, \{Ke Zhi\}",

year = "2013",

month = jul,

doi = "10.1016/j.corsci.2013.03.015",

language = "英语",

volume = "72",

pages = "150--155",

journal = "Corrosion Science",

issn = "0010-938X",

publisher = "Elsevier Ltd",

}

TY - JOUR

T1 - Microstructure and oxidation resistance of Si-Mo-B coating for C/SiC coated carbon/carbon composites

AU - Zhang, Yu Lei

AU - Li, He Jun

AU - Hu, Zhi Xiong

AU - Ren, Jin Cui

AU - Li, Ke Zhi

PY - 2013/7

Y1 - 2013/7

N2 - A self-sealing Si-Mo-B oxidation resistance coating was prepared on C/SiC coated carbon/carbon (C/C) composites by slurry and high temperature treatment method. The oxidation resistance of the coating increases at 1173. K and first increases then decreases at 1873. K with the increase of B content from 0 to 20. wt.%. The C/SiC/gradient Si-Mo-B multilayer coating can protect C/C composite from oxidation for 100. h at 1173. K and 125. h at 1873. K. The good oxidation resistance of the coating in broad temperature range could be attributed to its good self-sealing property.

AB - A self-sealing Si-Mo-B oxidation resistance coating was prepared on C/SiC coated carbon/carbon (C/C) composites by slurry and high temperature treatment method. The oxidation resistance of the coating increases at 1173. K and first increases then decreases at 1873. K with the increase of B content from 0 to 20. wt.%. The C/SiC/gradient Si-Mo-B multilayer coating can protect C/C composite from oxidation for 100. h at 1173. K and 125. h at 1873. K. The good oxidation resistance of the coating in broad temperature range could be attributed to its good self-sealing property.

KW - A. Ceramic matrix composites

KW - B. Weight loss

KW - C. Oxidation

UR - https://www.scopus.com/pages/publications/84877060511

U2 - 10.1016/j.corsci.2013.03.015

DO - 10.1016/j.corsci.2013.03.015

M3 - 文章

AN - SCOPUS:84877060511

SN - 0010-938X

VL - 72

SP - 150

EP - 155

JO - Corrosion Science

JF - Corrosion Science

ER -

Microstructure and oxidation resistance of Si-Mo-B coating for C/SiC coated carbon/carbon composites

摘要

访问文件

其它文件与链接

指纹

引用此