Microstructure and hydrogen storage properties of non-stoichiometric Zr-Ti-V Laves phase alloys

The non-stoichiometric C15 Laves phase alloys namely Zr _0.9Ti_0.1V_x (x = 1.7, 1.8, 1.9, 2.1, 2.2, 2.3) are designed and expected to investigate the role of defect and microstructure on hydrogenation kinetics of AB₂ type Zr-based alloys. The alloys are prepared by non-consumable arc melting in argon atmosphere and annealed at 1273 K for 168 h to ensure the homogeneity. The microstructure and phase constitute of these alloys are examined by SEM, TEM and XRD. The results indicate the homogenizing can reduce the minor phases α-Zr and abundant V solid solution originating from the non-equilibrium solidification of as-cast alloys. Twin defects with {111}<011 > orientation relationship are observed, and the role of defects on hydrogenation kinetics is discussed. Hydrogen absorption PCT characteristics and hydrogenation kinetics of Zr_0.9Ti _0.1V_x at 673-823 K are investigated by the pressure reduction method using a Sievert apparatus. The results show the hypo-stoichiometric alloys preserve faster hydrogenation kinetics than the hyper-stoichiometric ones due to the decrease of dendritic V. The excess content of Zr₃V₃O phase decreases the hydrogenation kinetics and the stability of hydrides. In addition, the different rate controlled mechanisms during hydrogen absorption are analyzed. The effects of non-stoichiometry on the crystal structure and hydrogen storage properties of Zr_0.9Ti _0.1V_x Laves alloys are discussed.