Liquid infiltration joining of C/SiC and Nb

Qiao Ying Tong; Lai Fei Cheng; Li Tong Zhang

Liquid infiltration joining of C/SiC and Nb

Qiao Ying Tong
, Lai Fei Cheng
, Li Tong Zhang

材料学院

Northwestern Polytechnical University Xian

科研成果: 期刊稿件 › 文章 › 同行评审

3 引用（Scopus）

摘要

Liquid infiltration joining of C/SiC composite with various woven style and Nb was studied. The join procedure was carried out at the temperature of 1300°C with the holding time of 45 min in vacuum. The pressure applied was 20 MPa. Ni-base interlinker was employed as the interlayer. Results showed joints of laminated C/SiC composite and Nb had been disjoined during the joints were cooled from the joining temperature to room temperature. However favorable joints of 3D C/SiC composite and Nb could be gained.

源语言	英语
页（从-至）	53-56
页数	4
期刊	Hangkong Cailiao Xuebao/Journal of Aeronautical Materials
卷	24
期	1
出版状态	已出版 - 2月 2004

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{cf8245afe8a54cc9a690cea78a2bcc1f,

title = "Liquid infiltration joining of C/SiC and Nb",

abstract = "Liquid infiltration joining of C/SiC composite with various woven style and Nb was studied. The join procedure was carried out at the temperature of 1300°C with the holding time of 45 min in vacuum. The pressure applied was 20 MPa. Ni-base interlinker was employed as the interlayer. Results showed joints of laminated C/SiC composite and Nb had been disjoined during the joints were cooled from the joining temperature to room temperature. However favorable joints of 3D C/SiC composite and Nb could be gained.",

keywords = "C/SiC, Composite, Liquid infiltration joining, Nb",

author = "Tong, \{Qiao Ying\} and Cheng, \{Lai Fei\} and Zhang, \{Li Tong\}",

year = "2004",

month = feb,

language = "英语",

volume = "24",

pages = "53--56",

journal = "Hangkong Cailiao Xuebao/Journal of Aeronautical Materials",

issn = "1005-5053",

publisher = "Science Press ",

number = "1",

}

TY - JOUR

T1 - Liquid infiltration joining of C/SiC and Nb

AU - Tong, Qiao Ying

AU - Cheng, Lai Fei

AU - Zhang, Li Tong

PY - 2004/2

Y1 - 2004/2

N2 - Liquid infiltration joining of C/SiC composite with various woven style and Nb was studied. The join procedure was carried out at the temperature of 1300°C with the holding time of 45 min in vacuum. The pressure applied was 20 MPa. Ni-base interlinker was employed as the interlayer. Results showed joints of laminated C/SiC composite and Nb had been disjoined during the joints were cooled from the joining temperature to room temperature. However favorable joints of 3D C/SiC composite and Nb could be gained.

AB - Liquid infiltration joining of C/SiC composite with various woven style and Nb was studied. The join procedure was carried out at the temperature of 1300°C with the holding time of 45 min in vacuum. The pressure applied was 20 MPa. Ni-base interlinker was employed as the interlayer. Results showed joints of laminated C/SiC composite and Nb had been disjoined during the joints were cooled from the joining temperature to room temperature. However favorable joints of 3D C/SiC composite and Nb could be gained.

KW - C/SiC

KW - Composite

KW - Liquid infiltration joining

KW - Nb

UR - https://www.scopus.com/pages/publications/2542520746

M3 - 文章

AN - SCOPUS:2542520746

SN - 1005-5053

VL - 24

SP - 53

EP - 56

JO - Hangkong Cailiao Xuebao/Journal of Aeronautical Materials

JF - Hangkong Cailiao Xuebao/Journal of Aeronautical Materials

IS - 1

ER -

Liquid infiltration joining of C/SiC and Nb

摘要

其它文件与链接

指纹

引用此