Large field-induced strain with enhanced temperature-stable dielectric properties of AgNbO₃-modified (Bi_0.5Na_0.5)_0.94Ba_0.06TiO₃ lead-free ceramics

(1-x)(Bi_0.5Na_0.5)_0.94Ba_0.06TiO₃-xAgNbO₃ lead-free piezoelectric ceramics (abbreviated as BNBT-100xAN) were prepared using the conventional solid-state sintering method. The effects of the introduction of AgNbO₃ (AN) dopants for the dielectric and piezoelectric performances of BNBT-100xAN ceramics were systematically studied. The XRD patterns and Raman spectra demonstrated that AN as a modifier was successfully diffused into the BNBT-100xAN lattice and revealed a pseudo-cubic symmetry structure. All samples exhibited a dense surface morphology accompanied by the uniform distribution of elements. A large bipolar strain of ~0.501% and unipolar strain of ~0.481% corresponding to the normalized strain d₃₃* of ~740 p.m./V were achieved for BNBT-1AN ceramic at 65 kV/cm field. The BNBT-4AN ceramic exhibited an excellent temperature-stable permittivity with the range from 59 to 380 °C and its dielectric loss was less than 0.02 between 97 °C and 329 °C. These results revealed that BNBT-100xAN ceramics were more hopeful candidates for actuators, strain sensors, and high-temperature capacitors.