Influence of preparation temperature on the oxidation resistance and mechanical properties of C/SiC coated C/C composites

A C/SiC oxidation resistance coating was prepared on carbon/carbon (C/C) composites by slurry and pack cementation. The microstructure, oxidation resistance and mechanical properties of C/SiC coating prepared from 1773 to 2573. K were investigated. With the increase of the preparation temperature, the oxidation resistance of C/SiC coating increases, however, the flexure strength decreases gradually. The preparation of C/SiC coating on C/C composites results in the fracture behavior of C/C composites changing from pseudo-plastic to brittle failure model. The decrease of flexure strength is mainly attributed to the decrease of C/C matrix' flexure strength at high temperature.