Improved fracture toughness of laminated ZrB₂-SiC-MoSi₂ ceramics using SiC whisker

In this study, SiC whisker (SiC_w) was introduced to ZrB₂ matrix layer of laminated ZrB₂/BN ceramics to improve fracture toughness. Laminated ZrB₂-SiC_w/BN ceramics were prepared by tape casting and spark plasma sintering. For comparison, monolithic ZrB₂-SiC_w and laminated ZrB₂-SiC_p/BN ceramics were also prepared using the same method. The introduction of SiC whiskers increased fracture toughness of laminated ZrB₂-SiC_w/BN ceramics to 13.31 ± 0.33 MPa m^1/2 for all samples. This was related to the multi-scale toughening mechanism, including delamination and crack deflection issued from the laminate structure at the macroscopic level, as well as whiskers bridging and pullout at the microscopic view. The R-curve behaviors of all samples revealed improved resistance to crack propagation of laminated ZrB₂-SiC_w/BN when compared to ZrB₂-SiC_p/BN and ZrB₂-SiC_w issued from multi-scale toughening design.