Friction and wear characteristics of lead and its compounds filled polytetrafluoroethylene composites under oil lubricated conditions

The friction and wear properties of Pb, PbO, Pb₃O₄, or PbS filled polytetrafluoroethylene (PTFE) composites sliding against GCr15 bearing steel under both dry and liquid paraffin lubricated conditions were studied by using an MHK-500 ring-block wear tester. The worn surfaces and the transfer films of these PTFE composites formed on the surface of GCr15 bearing steel were then investigated by using a scanning electron microscope (SEM) and an optical microscope, respectively. Experimental results show that filling Pb, PbO, Pb₃O₄ or PbS to PTFE can greatly reduce the wear of the PTFE composites, but the wear reducing action of Pb₃O₄ is the most effective. Meanwhile, PbS increases the friction coefficient of the PTFE composite, but Pb and Pb₃O₄ reduce the friction coefficients of the PTFE composites. However, the friction and wear properties of lead or its compounds filled PTFE composites can be greatly improved by lubrication with liquid paraffin, and the friction coefficients of the PTFE composites can be decreased by one order of magnitude. Optical microscope investigation of transfer films shows that Pb, PbO, Pb₃O₄ and PbS enhance the adhesion of the transfer films to the surface of GCr15 bearing steel, so they greatly reduce the wear of the PTFE composites. However, the transfer of the PTFE composites onto the surface of GCr15 bearing steel can be greatly reduced by lubrication with liquid paraffin, but the transfer still takes place. SEM examination of worn surfaces shows that the interaction between liquid paraffin and the PTFE composites creates some cracks on the worn surfaces of the PTFE composites; the creation and development of the cracks reduces the load-carrying capacity of the PTFE composites, and this leads to deterioration of the friction and wear properties of the PTFE composites filled with lead or its compounds under higher loads in liquid paraffin lubrication.