Enhanced energy storage properties and large electrostrictive effect of Bi_0.35Na_0.35Ba_0.09Sr_0.21Ti_(1-x)(Al_0.5Nb_0.5)_xO₃ relaxor ceramics

Ferroelectric ceramics have good piezoelectric and ferroelectric properties and can be used for energy storage equipment and actuators. Nevertheless, current research on dielectric capacitors has only focused on the energy storage density, but ignored efficiency. Moreover, conventional piezoelectric materials have a large strain hysteresis. In this work, (Al_0.5Nb_0.5)⁴⁺ (AN) complex ions doped 0.7Bi_0.5Na_0.5TiO₃-0.3Ba_0.3Sr_0.7TiO₃ (BNBST) ceramics were prepared. Doping AN destroyed the long-range ordered ferroelectric domains and generated polar nano regions, resulting in a gradual thinning and inclination of polarization hysteresis loops and an increase in relaxor degree. For BNBST-3AN ceramics, a W_rec of 1.52 J/cm³ and a η of 92.1% were achieved at 150 kV/cm. Meanwhile, BNBST-3AN ceramics had good energy storage temperature stability and cycling performance. The AN doping reduced the strain hysteresis in BNBST ceramics. BNBST-2AN ceramics exhibited a longitudinal electrostrictive coefficient Q₃₃ ∼ 0.0292 m⁴/C² and a field-induced strain of 0.25% with low strain hysteresis (6.67%). Furthermore, BNBST-4AN ceramics had superior dielectric temperature stability from 24 to 270 °C. All results show that BNBST-100xAN ceramics have great promise for energy storage devices and actuators.