Efficient multiscale strategy for toughening HfB₂ ceramics: A heterogeneous ceramic–metal layered architecture

A multiscale structural design was innovatively adopted herein to increase the toughness of monolithic HfB₂ ceramics. SiC whiskers (SiC_w) and graphene oxide (GO) were used as fillers for the HfB₂ matrix, whereas a ductile W foil was introduced as an interlayer to synthesize laminated HfB₂-SiC_w-rGO/W ceramics. Monolithic HfB₂-SiC_p (particulate) and laminated HfB₂-SiC_p/W ceramics were prepared using the same routes and used as controls. Following tape casting and spark plasma sintering at 1800°C, the toughness of the prepared laminated HfB₂-SiC_w-rGO/W samples was increased to 14.2 ± 0.6 MPa·m^1/2, with minimal sacrifice in flexural strength (421 ± 16 MPa). Morphological analysis of the fracture surface revealed the synergistic effects of micro-toughening (including bridging and pullout of whiskers and rGO) and macro-toughening (including crack deflection, bifurcation, and delamination) mechanisms responsible for improving the fracture toughness of the laminated HfB₂-SiC_w-rGO/W composites.