Effects of preparation conditions on the yield and embedding ratio of vinyl silicone oil microcapsules

Self-healing materials could repair themselves without external influences when they are damaged. In this paper, microcapsules are prepared by in-situ polymerization method, utilizing vinyl silicone oil as core material, polyurea formaldehyde as wall material and polyvinyl alcohol as dispersant. The morphology and structure of the microcapsules are tested with scanning electron microscopy, optical microscopy and laser particle analyzer. Effect of the reaction temperature, stirring speed and polyvinyl alcohol concentration on the yield, embedding ratio, particle size and its distribution are studied. Results show that the microcapsules can be successfully prepared by in-situ polymerization method. Under the reaction condition of temperature 60 °C, stirring speed 1000 r/min, dispersant concentration 0.1 wt.%, the yield and embedding ratio of the microcapsule are found to be 52.5% and 50.1%, respectively. The prepared microcapsules have smooth surface, good dispersibility, narrow particle size distribution and the average particle size is 13 μm.