Effect of pH on crystallization of nanocrystalline zirconia in a microwave-hydrothermal process

Haibo Ouyang; Cuiyan Li; Kezhi Li; Hejun Li; Yulei Zhang

doi:10.1007/s11595-016-1332-9

Effect of pH on crystallization of nanocrystalline zirconia in a microwave-hydrothermal process

Haibo Ouyang
, Cuiyan Li
, Kezhi Li
, Hejun Li
, Yulei Zhang

材料学院

Shaanxi University of Science and Technology

科研成果: 期刊稿件 › 文章 › 同行评审

23 引用（Scopus）

摘要

Nanocrystalline zirconia (ZrO₂) was synthesized using a microwave-hydrothermal process. The effect of pH on the crystallization of the ZrO₂ powders was investigated. The phase and microstructure of ZrO₂ powders were examined using X-ray diffraction (XRD), Raman spectroscopy, and transmission electron microscopy (TEM). Results show that pure m-ZrO₂ can be obtained at low pH (pH<2). Pure t-ZrO₂ is formed at pH = 7 and 14. The size of the ZrO₂ crystals is in the range of 8-26 nm and decreases with increasing pH. The formation of m-ZrO₂ results from the precipitation of ZrO₂ from solution. The t-ZrO₂ is formed through the in-situ structural rearrangement of amorphous Zr(OH)_xO_y. The stabilization of t-ZrO₂ is attributed to the small crystal size and the adsorption of hydroxy ions on the surfaces of the crystals.

源语言	英语
页（从-至）	68-73
页数	6
期刊	Journal Wuhan University of Technology, Materials Science Edition
卷	31
期	1
DOI	https://doi.org/10.1007/s11595-016-1332-9
出版状态	已出版 - 1 2月 2016

访问文件

10.1007/s11595-016-1332-9

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{901fd8f965dc49b68434d2c2306d1982,

title = "Effect of pH on crystallization of nanocrystalline zirconia in a microwave-hydrothermal process",

abstract = "Nanocrystalline zirconia (ZrO2) was synthesized using a microwave-hydrothermal process. The effect of pH on the crystallization of the ZrO2 powders was investigated. The phase and microstructure of ZrO2 powders were examined using X-ray diffraction (XRD), Raman spectroscopy, and transmission electron microscopy (TEM). Results show that pure m-ZrO2 can be obtained at low pH (pH<2). Pure t-ZrO2 is formed at pH = 7 and 14. The size of the ZrO2 crystals is in the range of 8-26 nm and decreases with increasing pH. The formation of m-ZrO2 results from the precipitation of ZrO2 from solution. The t-ZrO2 is formed through the in-situ structural rearrangement of amorphous Zr(OH)xOy. The stabilization of t-ZrO2 is attributed to the small crystal size and the adsorption of hydroxy ions on the surfaces of the crystals.",

keywords = "crystallization mechanism, microwave-hydrothermal, nanocrystalline zirconia, pH",

author = "Haibo Ouyang and Cuiyan Li and Kezhi Li and Hejun Li and Yulei Zhang",

note = "Publisher Copyright: {\textcopyright} 2016, Wuhan University of Technology and Springer-Verlag Berlin Heidelberg.",

year = "2016",

month = feb,

day = "1",

doi = "10.1007/s11595-016-1332-9",

language = "英语",

volume = "31",

pages = "68--73",

journal = "Journal Wuhan University of Technology, Materials Science Edition",

issn = "1000-2413",

publisher = "Springer Verlag",

number = "1",

}

TY - JOUR

T1 - Effect of pH on crystallization of nanocrystalline zirconia in a microwave-hydrothermal process

AU - Ouyang, Haibo

AU - Li, Cuiyan

AU - Li, Kezhi

AU - Li, Hejun

AU - Zhang, Yulei

PY - 2016/2/1

Y1 - 2016/2/1

N2 - Nanocrystalline zirconia (ZrO2) was synthesized using a microwave-hydrothermal process. The effect of pH on the crystallization of the ZrO2 powders was investigated. The phase and microstructure of ZrO2 powders were examined using X-ray diffraction (XRD), Raman spectroscopy, and transmission electron microscopy (TEM). Results show that pure m-ZrO2 can be obtained at low pH (pH<2). Pure t-ZrO2 is formed at pH = 7 and 14. The size of the ZrO2 crystals is in the range of 8-26 nm and decreases with increasing pH. The formation of m-ZrO2 results from the precipitation of ZrO2 from solution. The t-ZrO2 is formed through the in-situ structural rearrangement of amorphous Zr(OH)xOy. The stabilization of t-ZrO2 is attributed to the small crystal size and the adsorption of hydroxy ions on the surfaces of the crystals.

AB - Nanocrystalline zirconia (ZrO2) was synthesized using a microwave-hydrothermal process. The effect of pH on the crystallization of the ZrO2 powders was investigated. The phase and microstructure of ZrO2 powders were examined using X-ray diffraction (XRD), Raman spectroscopy, and transmission electron microscopy (TEM). Results show that pure m-ZrO2 can be obtained at low pH (pH<2). Pure t-ZrO2 is formed at pH = 7 and 14. The size of the ZrO2 crystals is in the range of 8-26 nm and decreases with increasing pH. The formation of m-ZrO2 results from the precipitation of ZrO2 from solution. The t-ZrO2 is formed through the in-situ structural rearrangement of amorphous Zr(OH)xOy. The stabilization of t-ZrO2 is attributed to the small crystal size and the adsorption of hydroxy ions on the surfaces of the crystals.

KW - crystallization mechanism

KW - microwave-hydrothermal

KW - nanocrystalline zirconia

KW - pH

UR - https://www.scopus.com/pages/publications/84957864423

U2 - 10.1007/s11595-016-1332-9

DO - 10.1007/s11595-016-1332-9

M3 - 文章

AN - SCOPUS:84957864423

SN - 1000-2413

VL - 31

SP - 68

EP - 73

JO - Journal Wuhan University of Technology, Materials Science Edition

JF - Journal Wuhan University of Technology, Materials Science Edition

IS - 1

ER -

Effect of pH on crystallization of nanocrystalline zirconia in a microwave-hydrothermal process

摘要

访问文件

其它文件与链接

学术指纹

引用此