Deformation Behavior and Microstructural Evolution Coordinated Regulation by Compression Deformation for Metastable Ti Alloy

In this paper, in order to investigate the harmonious relationship between the compression deformation behavior of metastable β titanium alloy and the microstructure evolution, the β solution-treated Ti-10V-2Fe-3Al (Ti-1023) alloy was compressed at room temperature and its deformation behavior was analyzed. Optical microscopy (OM) and field emission electron microscopy (FESEM) were used to study the microstructure evolution of alloys at different strain rates. The results show that the stress-induced martensite transformation (SIMT) is more easily activated by low strain rate compression deformation, which is conducive to improving its comprehensive mechanical properties. With the decrease in strain rate, the α″ martensite content increases significantly, the average grain size decreases substantially, and the Low Angle Grain Boundary (LAGB) volume fraction decreases correspondingly. In addition, after compression at different strain rates, the misorientation angle (MA) of the β matrix is mainly concentrated in the LAGBs. The change is small with the decrease in strain rate, but the α″ martensite orientation difference angle shows some peaks, which are ~60°, ~85°, and ~95°, respectively. Simultaneously, the strain rate has an important effect on the content and type of martensitic twins. Finally, the fracture morphology analysis shows that with the increase in strain rate, the fracture mode changes from ductile fracture to brittle fracture. The fracture surface presents a significantly elongated cavity along the direction of maximum shear stress.