Characterizations of cold-sprayed Nickel-Alumina composite coating with relatively large Nickel-coated Alumina powder

Previous studies have shown that the fabrication of metal matrix composites (MMCs) by cold spraying is effective and promising. When light materials, such as SiC and Al₂O₃, were used as reinforcements, it was diffcuclt to obtain a high volume fraction of hard phase in the composite just through the simple powder mixture. Therefore, in this study, a Ni-coated Al₂O₃ powder, which was produced through hydrothermal hydrogen reduction method, was employed aiming at increasing the volume fraction of ceramic particles in the deposited composite coating. It was found that a dense Ni-Al₂O₃ composite coating could be deposited with the Ni-coated Al₂O₃ powder under the present spray conditions. X-ray diffraction analysis indicated that the composite coating had the same phase structures as the feedstock. The volume fraction of Al₂O₃ in the composite was about 29 ± 6 vol.%, which is less than that in the feedstock (nominal: 40-45 vol.%) due to the rebound of some Al₂O₃ particulates upon kinetic impacting. The microhardness of the composite coating was about 173 ± 33Hv_0.2.