Changes in the structure and tribological property of Ag film by LEO space environment exposure

Ag films, deposited by arc ion plating, had been exposed for 43.5 h in real low earth orbit (LEO) space environment by a space environment exposure device (SEED) aboard the China Shenzhou-7 manned spaceship. The structure, morphology, composition and tribological property of the Ag films after the space environment exposure (SEE) were investigated using X-ray diffraction (XRD), field emission scanning electron microscope (FESEM), X-ray photoelectron spectroscope (XPS) and ball-on-disk tribometer, respectively. Depth XPS and XRD analysis revealed that after the SEE, the surface layer of Ag films was partially oxidized to Ag₂O, the cracking and flaking phenomena could be observed from the film surface by FESEM, and so the Ag films lose its metallic shine and became gray. As a result, the tribological performance was deteriorated and the high/unstable friction was obtained.