title = "Aging response of TB-13 titanium alloy",
abstract = "In order to develop a perspective of the new metastable β titanium alloy-TB-13, the influence of ageing treatments on the microstructure and properties has been studied. The results show that TB-13 alloy displays high age strengthening effect and fine precipitation. During the one-step aging process, the higher the aging temperature, the coarser the α plate thickness. As a result, TB-13 alloy shows the lower the strength and the higher the ductility. The best combination of strength and ductility is acquired in the TB-13 alloy after solution treatment at 1133K following aging at 813K for 16h. The ultimate strength is near 1400MPa and the specific elongation is 7.0\% by ageing. At last, the details of the transformation mechanism and microstructural evolution accompanying ω-assisted α nucleation during continuous heating are discussed.",
keywords = "Aging, Nucleation, Precipitate, Titanium alloy",
author = "Zhongbo Zhou and Jinshan Li and Hongchao Kou and Zhishou Zhu and Bin Tang and Hui Chang",
year = "2010",
doi = "10.4028/www.scientific.net/MSF.654-656.859",
language = "英语",
isbn = "0878492550",
series = "Materials Science Forum",
publisher = "Trans Tech Publications Ltd",
pages = "859--862",
booktitle = "PRICM7",
note = "7th Pacific Rim International Conference on Advanced Materials and Processing, PRICM-7 ; Conference date: 02-08-2010 Through 06-08-2010",
}