A study of Ni3Si-based composite coating fabricated by self-propagating high temperature synthesis casting route

Muye Niu; Qinling Bi; Lingqian Kong; Jun Yang; Weimin Liu

doi:10.1016/j.surfcoat.2011.03.031

A study of Ni₃Si-based composite coating fabricated by self-propagating high temperature synthesis casting route

Muye Niu
, Qinling Bi
, Lingqian Kong
, Jun Yang
, Weimin Liu

CAS - Lanzhou Institute of Chemical Physics
University of Chinese Academy of Sciences

科研成果: 期刊稿件 › 文章 › 同行评审

26 引用（Scopus）

摘要

A Ni₃Si-Cr₇C₃ composite coating was fabricated on AISI 1020 steel substrate by self-propagating high-temperature synthesis (SHS) casting route. Phase composition, microhardness and dry sliding wear behavior of the coating were studied. The results indicated that the coating was mainly consisted of Ni₃Si and Cr₇C₃. The microhardness of coating is about 900HV. The friction and wear tests showed that although the friction coefficient had no obvious change, the wear resistance of the AISI 1020 steel matrix was improved greatly. Also, the corrosion test result showed that the coating had an excellent corrosion resistance.

源语言	英语
页（从-至）	4249-4253
页数	5
期刊	Surface and Coatings Technology
卷	205
期	17-18
DOI	https://doi.org/10.1016/j.surfcoat.2011.03.031
出版状态	已出版 - 25 5月 2011
已对外发布	是

访问文件

10.1016/j.surfcoat.2011.03.031

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{c25d19c034744f6cb6822d08ada57a37,

title = "A study of Ni3Si-based composite coating fabricated by self-propagating high temperature synthesis casting route",

abstract = "A Ni3Si-Cr7C3 composite coating was fabricated on AISI 1020 steel substrate by self-propagating high-temperature synthesis (SHS) casting route. Phase composition, microhardness and dry sliding wear behavior of the coating were studied. The results indicated that the coating was mainly consisted of Ni3Si and Cr7C3. The microhardness of coating is about 900HV. The friction and wear tests showed that although the friction coefficient had no obvious change, the wear resistance of the AISI 1020 steel matrix was improved greatly. Also, the corrosion test result showed that the coating had an excellent corrosion resistance.",

keywords = "Coating, Nickel-silicide, SHS, Wear resistance",

author = "Muye Niu and Qinling Bi and Lingqian Kong and Jun Yang and Weimin Liu",

year = "2011",

month = may,

day = "25",

doi = "10.1016/j.surfcoat.2011.03.031",

language = "英语",

volume = "205",

pages = "4249--4253",

journal = "Surface and Coatings Technology",

issn = "0257-8972",

publisher = "Elsevier B.V.",

number = "17-18",

}

TY - JOUR

T1 - A study of Ni3Si-based composite coating fabricated by self-propagating high temperature synthesis casting route

AU - Niu, Muye

AU - Bi, Qinling

AU - Kong, Lingqian

AU - Yang, Jun

AU - Liu, Weimin

PY - 2011/5/25

Y1 - 2011/5/25

N2 - A Ni3Si-Cr7C3 composite coating was fabricated on AISI 1020 steel substrate by self-propagating high-temperature synthesis (SHS) casting route. Phase composition, microhardness and dry sliding wear behavior of the coating were studied. The results indicated that the coating was mainly consisted of Ni3Si and Cr7C3. The microhardness of coating is about 900HV. The friction and wear tests showed that although the friction coefficient had no obvious change, the wear resistance of the AISI 1020 steel matrix was improved greatly. Also, the corrosion test result showed that the coating had an excellent corrosion resistance.

AB - A Ni3Si-Cr7C3 composite coating was fabricated on AISI 1020 steel substrate by self-propagating high-temperature synthesis (SHS) casting route. Phase composition, microhardness and dry sliding wear behavior of the coating were studied. The results indicated that the coating was mainly consisted of Ni3Si and Cr7C3. The microhardness of coating is about 900HV. The friction and wear tests showed that although the friction coefficient had no obvious change, the wear resistance of the AISI 1020 steel matrix was improved greatly. Also, the corrosion test result showed that the coating had an excellent corrosion resistance.

KW - Coating

KW - Nickel-silicide

KW - SHS

KW - Wear resistance

UR - https://www.scopus.com/pages/publications/79955118678

U2 - 10.1016/j.surfcoat.2011.03.031

DO - 10.1016/j.surfcoat.2011.03.031

M3 - 文章

AN - SCOPUS:79955118678

SN - 0257-8972

VL - 205

SP - 4249

EP - 4253

JO - Surface and Coatings Technology

JF - Surface and Coatings Technology

IS - 17-18

ER -

A study of Ni3Si-based composite coating fabricated by self-propagating high temperature synthesis casting route

摘要

访问文件

其它文件与链接

指纹

引用此

A study of Ni₃Si-based composite coating fabricated by self-propagating high temperature synthesis casting route