Supercondcuting properties in MgB2/Fe wires prepared by PIT method

Guo Yan; Yonq Feng; Baoquan Fu; Chunfang Liu; Ping Ji; Pingxiang Zhang; Lian Zhou

doi:10.1360/02ww0261

Supercondcuting properties in MgB₂/Fe wires prepared by PIT method

Guo Yan
, Yonq Feng
, Baoquan Fu
, Chunfang Liu
, Ping Ji
, Pingxiang Zhang
, Lian Zhou

Northeastern University China
Northwest Institute for Nonferrous Metal Research

Research output: Contribution to journal › Article › peer-review

3 Scopus citations

Abstract

The MgB₂ formation was analyzed physically and chemically and the MgB₂/Fe wires were fabricated by powder in tube (PIT) technology. The microstructure of MgB₂ in wires was studied by the scanning electrical microscope (SEM), which shows a good connection of grains and the size of MgB₂ grain is 1-3 μm. The results of J_c measured by the standard four probes method show that J_c value reaches 6.1×10⁴ A/cm² at 20 K in self field.

Original language	English
Pages (from-to)	1331-1333
Number of pages	3
Journal	Chinese Science Bulletin
Volume	48
Issue number	13
DOIs	https://doi.org/10.1360/02ww0261
State	Published - 2003
Externally published	Yes

Keywords

Critical current density
In-situ PIT
MgB
Wires

Access to Document

10.1360/02ww0261

Cite this

@article{a92924a5e0e44c5e834b3ad94bcc0519,

title = "Supercondcuting properties in MgB2/Fe wires prepared by PIT method",

abstract = "The MgB2 formation was analyzed physically and chemically and the MgB2/Fe wires were fabricated by powder in tube (PIT) technology. The microstructure of MgB2 in wires was studied by the scanning electrical microscope (SEM), which shows a good connection of grains and the size of MgB2 grain is 1-3 μm. The results of Jc measured by the standard four probes method show that Jc value reaches 6.1×104 A/cm2 at 20 K in self field.",

keywords = "Critical current density, In-situ PIT, MgB, Wires",

author = "Guo Yan and Yonq Feng and Baoquan Fu and Chunfang Liu and Ping Ji and Pingxiang Zhang and Lian Zhou",

year = "2003",

doi = "10.1360/02ww0261",

language = "英语",

volume = "48",

pages = "1331--1333",

journal = "Chinese Science Bulletin",

issn = "1001-6538",

publisher = "Science Press ",

number = "13",

}

TY - JOUR

T1 - Supercondcuting properties in MgB2/Fe wires prepared by PIT method

AU - Yan, Guo

AU - Feng, Yonq

AU - Fu, Baoquan

AU - Liu, Chunfang

AU - Ji, Ping

AU - Zhang, Pingxiang

AU - Zhou, Lian

PY - 2003

Y1 - 2003

N2 - The MgB2 formation was analyzed physically and chemically and the MgB2/Fe wires were fabricated by powder in tube (PIT) technology. The microstructure of MgB2 in wires was studied by the scanning electrical microscope (SEM), which shows a good connection of grains and the size of MgB2 grain is 1-3 μm. The results of Jc measured by the standard four probes method show that Jc value reaches 6.1×104 A/cm2 at 20 K in self field.

AB - The MgB2 formation was analyzed physically and chemically and the MgB2/Fe wires were fabricated by powder in tube (PIT) technology. The microstructure of MgB2 in wires was studied by the scanning electrical microscope (SEM), which shows a good connection of grains and the size of MgB2 grain is 1-3 μm. The results of Jc measured by the standard four probes method show that Jc value reaches 6.1×104 A/cm2 at 20 K in self field.

KW - Critical current density

KW - In-situ PIT

KW - MgB

KW - Wires

UR - https://www.scopus.com/pages/publications/33749850390

U2 - 10.1360/02ww0261

DO - 10.1360/02ww0261

M3 - 文章

AN - SCOPUS:33749850390

SN - 1001-6538

VL - 48

SP - 1331

EP - 1333

JO - Chinese Science Bulletin

JF - Chinese Science Bulletin

IS - 13