MoS₂ powders coated with Y-TZP were prepared by heating alcohol-water solution of ZrOCl₂·8H₂O and Y(NO₃)₃·6H₂O with particles of MoS2. Y-TZP/MoS₂ composites with special microstructure and good mechanical properties were fabricated by hot pressing sinter. The tribological properties of Y-TZP/MoS₂ composites sliding against ZrO₂ at room temperature were investigated. Results show that the friction coefficient of the composite with 44wt% MoS₂ added is as low as 0.25, and the wear rate of the composite is 1.05×l0^-6 mm³/mN.

Original language	English
Pages (from-to)	207-213
Number of pages	7
Journal	Wuji Cailiao Xuebao/Journal of Inorganic Materials
Volume	19
Issue number	1
State	Published - Jan 2004
Externally published	Yes

Keywords

Coated
Self-lubrication ceramic
Y-TZP: MoS

Cite this

@article{61e47130b4454e37b97d920bba6e1a74,

title = "Study on self-lubrication ceramic of Y-TZP/MoS2",

abstract = "MoS2 powders coated with Y-TZP were prepared by heating alcohol-water solution of ZrOCl2·8H2O and Y(NO3)3·6H2O with particles of MoS2. Y-TZP/MoS2 composites with special microstructure and good mechanical properties were fabricated by hot pressing sinter. The tribological properties of Y-TZP/MoS2 composites sliding against ZrO2 at room temperature were investigated. Results show that the friction coefficient of the composite with 44wt\% MoS2 added is as low as 0.25, and the wear rate of the composite is 1.05×l0-6 mm3/mN.",

keywords = "Coated, Self-lubrication ceramic, Y-TZP: MoS",

author = "Liang, \{Hong Xun\} and Lu, \{Jin Jun\} and Liu, \{Wei Min\} and Xue, \{Qun Ji\}",

year = "2004",

month = jan,

language = "英语",

volume = "19",

pages = "207--213",

journal = "Wuji Cailiao Xuebao/Journal of Inorganic Materials",

issn = "1000-324X",

publisher = "Science Press ",

number = "1",

}

TY - JOUR

T1 - Study on self-lubrication ceramic of Y-TZP/MoS2

AU - Liang, Hong Xun

AU - Lu, Jin Jun

AU - Liu, Wei Min

AU - Xue, Qun Ji

PY - 2004/1

Y1 - 2004/1

N2 - MoS2 powders coated with Y-TZP were prepared by heating alcohol-water solution of ZrOCl2·8H2O and Y(NO3)3·6H2O with particles of MoS2. Y-TZP/MoS2 composites with special microstructure and good mechanical properties were fabricated by hot pressing sinter. The tribological properties of Y-TZP/MoS2 composites sliding against ZrO2 at room temperature were investigated. Results show that the friction coefficient of the composite with 44wt% MoS2 added is as low as 0.25, and the wear rate of the composite is 1.05×l0-6 mm3/mN.

AB - MoS2 powders coated with Y-TZP were prepared by heating alcohol-water solution of ZrOCl2·8H2O and Y(NO3)3·6H2O with particles of MoS2. Y-TZP/MoS2 composites with special microstructure and good mechanical properties were fabricated by hot pressing sinter. The tribological properties of Y-TZP/MoS2 composites sliding against ZrO2 at room temperature were investigated. Results show that the friction coefficient of the composite with 44wt% MoS2 added is as low as 0.25, and the wear rate of the composite is 1.05×l0-6 mm3/mN.

KW - Coated

KW - Self-lubrication ceramic

KW - Y-TZP: MoS

UR - https://www.scopus.com/pages/publications/1942507421

M3 - 文章

AN - SCOPUS:1942507421

SN - 1000-324X

VL - 19

SP - 207

EP - 213

JO - Wuji Cailiao Xuebao/Journal of Inorganic Materials

JF - Wuji Cailiao Xuebao/Journal of Inorganic Materials

IS - 1

ER -

Study on self-lubrication ceramic of Y-TZP/MoS₂

Abstract

Keywords

Other files and links

Fingerprint

Cite this