Structure and oxidation behavior of a plasma sprayed yttrium silicates coated SiC-C/C with a glass outer sealant from 1 573K to 1 873K

Jianfeng Huang; Hejun Li; Xierong Zeng; Liyun Cao; Kezhi Li; Xinbo Xiong; Long Li

doi:10.1007/s11595-006-1033-x

Structure and oxidation behavior of a plasma sprayed yttrium silicates coated SiC-C/C with a glass outer sealant from 1 573K to 1 873K

Jianfeng Huang
, Hejun Li
, Xierong Zeng
, Liyun Cao
, Kezhi Li
, Xinbo Xiong
, Long Li

School of Materials Sience and Engineering

Shaanxi University of Science and Technology
Northwestern Polytechnical University Xian
Shenzhen University

Research output: Contribution to journal › Article › peer-review

5 Scopus citations

Abstract

Different compositions of yttrium silicates coatings were deposited on SiC-C/C by plasma spraying and an outer borosilicate glass was applied on the yttrium silicates coatings surfaces. The structure of the multi-layer coatings was characterized by XRD and SEM analyses. High temperature oxidation behavior of the multi-layer coatings coated C/C composites was investigated. Results show that SiC/2SiO₂•Y₂O₃/1.5SiO ₂•Y₂O₃/ SiO₂•Y ₂O₃/glass multi-layer coating has better high temperature oxidation resistance, protecting carbon/ carbon composites from oxidation at 1 773 K in air for 164 h with the weight loss of 1.65%. The oxidation weight loss of the coated C/C with time accorded with parabolic rule in the temperature range 1 573 K-1 873 K; and the corresponding oxidation activation energy of the coated carbon/carbon composites is 132.2 kJ/mol.

Original language	English
Pages (from-to)	33-37
Number of pages	5
Journal	Journal Wuhan University of Technology, Materials Science Edition
Volume	23
Issue number	1
DOIs	https://doi.org/10.1007/s11595-006-1033-x
State	Published - Feb 2008

Keywords

Carbon/carbon composites
Coating
Oxidation behavior
Plasma spraying

Access to Document

10.1007/s11595-006-1033-x

Cite this

@article{ec2a19e5a36c4ead878db02fc9fe77ea,

title = "Structure and oxidation behavior of a plasma sprayed yttrium silicates coated SiC-C/C with a glass outer sealant from 1 573K to 1 873K",

abstract = "Different compositions of yttrium silicates coatings were deposited on SiC-C/C by plasma spraying and an outer borosilicate glass was applied on the yttrium silicates coatings surfaces. The structure of the multi-layer coatings was characterized by XRD and SEM analyses. High temperature oxidation behavior of the multi-layer coatings coated C/C composites was investigated. Results show that SiC/2SiO2•Y2O3/1.5SiO 2•Y2O3/ SiO2•Y 2O3/glass multi-layer coating has better high temperature oxidation resistance, protecting carbon/ carbon composites from oxidation at 1 773 K in air for 164 h with the weight loss of 1.65\%. The oxidation weight loss of the coated C/C with time accorded with parabolic rule in the temperature range 1 573 K-1 873 K; and the corresponding oxidation activation energy of the coated carbon/carbon composites is 132.2 kJ/mol.",

keywords = "Carbon/carbon composites, Coating, Oxidation behavior, Plasma spraying",

author = "Jianfeng Huang and Hejun Li and Xierong Zeng and Liyun Cao and Kezhi Li and Xinbo Xiong and Long Li",

year = "2008",

month = feb,

doi = "10.1007/s11595-006-1033-x",

language = "英语",

volume = "23",

pages = "33--37",

journal = "Journal Wuhan University of Technology, Materials Science Edition",

issn = "1000-2413",

publisher = "Springer Verlag",

number = "1",

}

TY - JOUR

T1 - Structure and oxidation behavior of a plasma sprayed yttrium silicates coated SiC-C/C with a glass outer sealant from 1 573K to 1 873K

AU - Huang, Jianfeng

AU - Li, Hejun

AU - Zeng, Xierong

AU - Cao, Liyun

AU - Li, Kezhi

AU - Xiong, Xinbo

AU - Li, Long

PY - 2008/2

Y1 - 2008/2

N2 - Different compositions of yttrium silicates coatings were deposited on SiC-C/C by plasma spraying and an outer borosilicate glass was applied on the yttrium silicates coatings surfaces. The structure of the multi-layer coatings was characterized by XRD and SEM analyses. High temperature oxidation behavior of the multi-layer coatings coated C/C composites was investigated. Results show that SiC/2SiO2•Y2O3/1.5SiO 2•Y2O3/ SiO2•Y 2O3/glass multi-layer coating has better high temperature oxidation resistance, protecting carbon/ carbon composites from oxidation at 1 773 K in air for 164 h with the weight loss of 1.65%. The oxidation weight loss of the coated C/C with time accorded with parabolic rule in the temperature range 1 573 K-1 873 K; and the corresponding oxidation activation energy of the coated carbon/carbon composites is 132.2 kJ/mol.

AB - Different compositions of yttrium silicates coatings were deposited on SiC-C/C by plasma spraying and an outer borosilicate glass was applied on the yttrium silicates coatings surfaces. The structure of the multi-layer coatings was characterized by XRD and SEM analyses. High temperature oxidation behavior of the multi-layer coatings coated C/C composites was investigated. Results show that SiC/2SiO2•Y2O3/1.5SiO 2•Y2O3/ SiO2•Y 2O3/glass multi-layer coating has better high temperature oxidation resistance, protecting carbon/ carbon composites from oxidation at 1 773 K in air for 164 h with the weight loss of 1.65%. The oxidation weight loss of the coated C/C with time accorded with parabolic rule in the temperature range 1 573 K-1 873 K; and the corresponding oxidation activation energy of the coated carbon/carbon composites is 132.2 kJ/mol.

KW - Carbon/carbon composites

KW - Coating

KW - Oxidation behavior

KW - Plasma spraying

UR - https://www.scopus.com/pages/publications/38949153094

U2 - 10.1007/s11595-006-1033-x

DO - 10.1007/s11595-006-1033-x

M3 - 文章

AN - SCOPUS:38949153094

SN - 1000-2413

VL - 23

SP - 33

EP - 37

JO - Journal Wuhan University of Technology, Materials Science Edition

JF - Journal Wuhan University of Technology, Materials Science Edition

IS - 1

ER -

Structure and oxidation behavior of a plasma sprayed yttrium silicates coated SiC-C/C with a glass outer sealant from 1 573K to 1 873K

Abstract

Keywords

Access to Document

Other files and links

Fingerprint

Cite this