Strain properties of (1-x)Bi_0.5Na_0.4K_0.1TiO₃-xBi(Mg_2/3Ta_1/3)O₃ electroceramics

A ternary solid solution of Bi_0.5Na_0.5TiO₃–Bi_0.5K_0.5TiO₃–Bi(Mg_2/3Ta_1/3)O₃ (BNKT-xBMT) lead-free electroceramics was synthesized by a solid-state reactive sintering technique. The electrostrain, dielectric, and ferroelectric properties as well as the impedance characteristics and the microstructure were systematically assessed. With the increase of BMT, the BNKT-xBMT ceramics gradually transformed from non-ergodic relaxor phase to ergodic relaxor phase, manifested as the ferroelectric-to-relaxor temperature (T_F-R) shifts towards below room temperature. Additionally, the ferroelectric hysteresis curves became pinched, and the strain curve changed from butterfly-shaped into sprout-shaped. At the ergodic relaxor composition of x = 0.04, a large electrostrain value (S = 0.4%; under an electric field of 60 kV/cm, d₃₃* = 632 pm/V) was achieved, which is mainly attributed to the electric-field-induced transition from the ergodic relaxor phase to the ferroelectric phase.