Preparation and characterization of relaxor-based ferroelectric thick films with single perovskite structure

Huiqing Fan; Jin Chen; Xiuli Chen

doi:10.4028/0-87849-473-1.24

Preparation and characterization of relaxor-based ferroelectric thick films with single perovskite structure

Huiqing Fan, Jin Chen, Xiuli Chen

School of Materials Sience and Engineering

Northwestern Polytechnical University Xian

Research output: Contribution to journal › Article › peer-review

2 Scopus citations

Abstract

Lead magnesium niobate-lead titanate (0.8Pb(Mg_1/3Nb _2/3)O₃-0.2PbTiO₃, PMN-PT) thick films in the thickness range about 75 μm have been successfully fabricated on Au-coated Al₂O₃ substrates by electrophoretic deposition (EPD). Non-aqueous colloidal suspensions suitable for EPD were prepared by mixing ultrasonically PMN-PT particles in ethanol with pH=6.0. The effect of EPD process parameters such as deposition voltage, deposition time and the specific deposition mass of PMN-PT particles were investigated. The EPD parameters were optimized in order to obtain crack-free, high-quality uniform ceramic films. The deposited pyrochlore-free PMN-PT thick films were sintered at 1000°C for 30 min, and the phase evolvement and the microstructure of the film were characterized by X-ray diffraction and scanning electron microscope.

Original language	English
Pages (from-to)	24-26
Number of pages	3
Journal	Key Engineering Materials
Volume	368-372 PART 1
DOIs	https://doi.org/10.4028/0-87849-473-1.24
State	Published - 2008

Keywords

Electrophoretic deposition
Perovskite
PMN-PT
Thick films

Access to Document

10.4028/0-87849-473-1.24

Cite this

@article{2e31056ca15041ba9f5b102212cb690e,

title = "Preparation and characterization of relaxor-based ferroelectric thick films with single perovskite structure",

abstract = "Lead magnesium niobate-lead titanate (0.8Pb(Mg1/3Nb 2/3)O3-0.2PbTiO3, PMN-PT) thick films in the thickness range about 75 μm have been successfully fabricated on Au-coated Al2O3 substrates by electrophoretic deposition (EPD). Non-aqueous colloidal suspensions suitable for EPD were prepared by mixing ultrasonically PMN-PT particles in ethanol with pH=6.0. The effect of EPD process parameters such as deposition voltage, deposition time and the specific deposition mass of PMN-PT particles were investigated. The EPD parameters were optimized in order to obtain crack-free, high-quality uniform ceramic films. The deposited pyrochlore-free PMN-PT thick films were sintered at 1000°C for 30 min, and the phase evolvement and the microstructure of the film were characterized by X-ray diffraction and scanning electron microscope.",

keywords = "Electrophoretic deposition, Perovskite, PMN-PT, Thick films",

author = "Huiqing Fan and Jin Chen and Xiuli Chen",

year = "2008",

doi = "10.4028/0-87849-473-1.24",

language = "英语",

volume = "368-372 PART 1",

pages = "24--26",

journal = "Key Engineering Materials",

issn = "1013-9826",

publisher = "Trans Tech Publications Ltd",

}

TY - JOUR

T1 - Preparation and characterization of relaxor-based ferroelectric thick films with single perovskite structure

AU - Fan, Huiqing

AU - Chen, Jin

AU - Chen, Xiuli

PY - 2008

Y1 - 2008

N2 - Lead magnesium niobate-lead titanate (0.8Pb(Mg1/3Nb 2/3)O3-0.2PbTiO3, PMN-PT) thick films in the thickness range about 75 μm have been successfully fabricated on Au-coated Al2O3 substrates by electrophoretic deposition (EPD). Non-aqueous colloidal suspensions suitable for EPD were prepared by mixing ultrasonically PMN-PT particles in ethanol with pH=6.0. The effect of EPD process parameters such as deposition voltage, deposition time and the specific deposition mass of PMN-PT particles were investigated. The EPD parameters were optimized in order to obtain crack-free, high-quality uniform ceramic films. The deposited pyrochlore-free PMN-PT thick films were sintered at 1000°C for 30 min, and the phase evolvement and the microstructure of the film were characterized by X-ray diffraction and scanning electron microscope.

AB - Lead magnesium niobate-lead titanate (0.8Pb(Mg1/3Nb 2/3)O3-0.2PbTiO3, PMN-PT) thick films in the thickness range about 75 μm have been successfully fabricated on Au-coated Al2O3 substrates by electrophoretic deposition (EPD). Non-aqueous colloidal suspensions suitable for EPD were prepared by mixing ultrasonically PMN-PT particles in ethanol with pH=6.0. The effect of EPD process parameters such as deposition voltage, deposition time and the specific deposition mass of PMN-PT particles were investigated. The EPD parameters were optimized in order to obtain crack-free, high-quality uniform ceramic films. The deposited pyrochlore-free PMN-PT thick films were sintered at 1000°C for 30 min, and the phase evolvement and the microstructure of the film were characterized by X-ray diffraction and scanning electron microscope.

KW - Electrophoretic deposition

KW - Perovskite

KW - PMN-PT

KW - Thick films

UR - https://www.scopus.com/pages/publications/40949160153

U2 - 10.4028/0-87849-473-1.24

DO - 10.4028/0-87849-473-1.24

M3 - 文章

AN - SCOPUS:40949160153

SN - 1013-9826

VL - 368-372 PART 1

SP - 24

EP - 26

JO - Key Engineering Materials

JF - Key Engineering Materials

ER -

Preparation and characterization of relaxor-based ferroelectric thick films with single perovskite structure

Abstract

Keywords

Access to Document

Other files and links

Fingerprint

Cite this