Microstructural characterization and abrasive wear performance of HVOF sprayed Cr₃C₂-NiCr coating

Cr₃C₂-NiCr coatings were deposited by high velocity oxy-fuel (HVOF) process with different spray parameters to examine dominant microstructural factors in abrasive wear of the coatings. The microstructure of the HVOF sprayed Cr₃C₂-NiCr coatings was characterized by scanning electron microscopy and transmission electron microscopy (TEM). The apparent average size and volume fraction of carbide particles in the coatings were estimated through a quantitative imaging analysis. The formation of carbide phases in the coating was discussed based on the TEM observation results. The abrasive wear behavior of the coating was evaluated by the dry rubber wheel abrasive wear test and the wear mechanisms were elucidated. Influences of apparent size and volume fraction of carbide particles on the abrasive wear weight loss were examined through correlating the proposed relation with the experimental results. Results showed that Cr₃C₂ particle size was significantly reduced after the spraying and Cr₇C₃ carbide was present around Cr₃C₂ particles, and Cr₂₃C₆ carbide was dispersed in NiCr alloy matrix with a nano-crystalline structure. The three carbides were formed in the coating through different mechanisms. The removal of carbide particles in the coating was mainly responsible for the abrasive wear of the coating. The content and particle size of the Cr₃C₂ carbides were the two key factors controlling the abrasive wear of the HVOF sprayed Cr₃C₂-NiCr coatings.