title = "Investigation on the corrosion effect of friction stir welded AA2024 T3 aluminum alloy joints",
abstract = "Before friction stir welded integral panels are used in main aircraft structure, the corrosion behavior of welded joint need to be studied in detail. 2024 T3 samples were designed and welded by friction stir welding; the microstructure crossing the weld zone was observed by scanning electron microscopy (SEM), the feature of different zones (base material, thermo-mechanical affected zone, nugget) was seen; the corrosion testing in NaCl smoking box was carried out, and microstructure was observed after corrosion, localized corrosion predominantly occurs in the thermo-mechanical affected zone.",
keywords = "Corrosion behavior, Friction stir weld, Microstructure of nugget",
author = "Ma, \{Yu E.\} and Zhao, \{Zhen Qiang\}",
year = "2012",
doi = "10.4028/www.scientific.net/KEM.525-526.129",
language = "英语",
isbn = "9783037854631",
series = "Key Engineering Materials",
publisher = "Trans Tech Publications Ltd",
pages = "129--132",
booktitle = "Advances in Fracture and Damage Mechanics XI",
note = "11th International Conference on Fracture and Damage Mechanics, FDM 2012 ; Conference date: 18-09-2012 Through 21-09-2012",
}