Effects of Zn addition on the improvement of glass forming ability and plasticity of Mg-Cu-Tb bulk metallic glasses

The effects of Zn addition on the glass forming ability and mechanical properties of Mg₆₅Cu_25-xZn_xTb₁₀ (x = 0, 2.5, 5, and 7.5) have been investigated. We show that small amounts of Zn addition improve the glass forming ability, strength, and ductility of the Mg-Cu-Tb bulk metallic glass. For the best glass forming composition, amorphous rods of Mg₆₅Cu₂₀Zn₅Tb₁₀ with a diameter of at least 7 mm have been prepared by a conventional copper mold casting method. Additionally, this composition exhibits obvious yielding and plastic deformation upon quasi-static compressive loading. The fracture strength, total strain to failure, and the plastic strain of the Mg₆₅Cu₂₀Zn₅Tb₁₀ bulk metallic glass reaches 1025 MPa, 2.05% and 0.15%, respectively. This is significantly superior compared to that exhibited by the original Zn-free Mg-Cu-Tb amorphous alloy.