Effect of Ti addition on the microstructure and corrosion behavior of laser cladding AlCoCrFeNi high-entropy alloy coatings

AlCoCrFeNi high-entropy alloys (HEAs) has higher strength and wear resistance but poorer corrosion resistance. In the present investigation, the AlCoCrFeNi HEAs containing titanium(Ti) were fabricated via laser cladding to enhance the corrosion resistance properties of the coating and the influence of the Ti content on the microstructure of the coatings was investigated. The results show that the microstructure of the coating changed from a single BCC phase to a BCC + B2 phase with the addition of Ti. The Laves phases appeared within the coating when the Ti content was beyond 0.5 mol ratio. As an excellent corrosion-resistant element, Ti promoted the formation of a passive film and enhanced the corrosion resistance of the HEAs coating. The corrosion resistance of the coating first increased and then decreased with the addition of Ti, and the AlCoCrFeNiTi_0.5 coating exhibited optimal corrosion resistance.