Corrigendum to “Microstructural evolution of coating-modified 3D C/SiC composites after annealing in wet oxygen at different temperatures” [Corros. Sci. 52 (2010) 2837–2845, (S0010938X10002192), (10.1016/j.corsci.2010.04.032)]

The authors regret that some pictures inFig. 2, Fig. 3, Fig. 4, Fig. 6, Fig. 9 and Fig. 11 are incorrectly published, the correct figures with more appropriate captions are provided below. Also, two sentences in the manuscript should be revised. (1) In paragraph 5 in p. 2838, the width of healed defects (refers to Fig. 3d) “is only about 500 nm” should be “is observed at about 600 nm”.(2) In paragraph 6 in p. 2838, the dimension of crack healing (refers to Fig. 4a) published as 1 µm should instead as ∼ 2 µm.The conclusions drawn in the paper are unaffected by these changes.