Abnormal Decrease in Fatigue Properties of DD6 Single Crystal Superalloy After Hot Isostatic Pressing

The abnormal effect of hot isostatic pressing (HIP) on the fatigue properties of DD6 single crystal superalloy was investigated. The results showed that HIP combined with standard heat treatment (SHT) reduced the fatigue life under 880 °C and 800 MPa. HIP treatment eliminated inner shrinkage porosity effectively; however, the amount of micropores increased in the subsequent SHT. Moreover, HIP treatment enlarged the size of γ′ precipitates gradually and altered the morphology of carbides greatly. Small MC carbides decomposed into M₂₃C₆ carbides, and a serrated structure formed on the surface of large-size MC carbides, which led to the positive and negative effects on fatigue properties, respectively, depending on the morphology and size of carbides. Recrystallized microstructures were observed after HIP treatment, accompanied by fine, continuous precipitates along recrystallized grain boundaries. This led to a sharp decline in the elevated-temperature fatigue properties of DD6 superalloy fabricated at a drawing velocity of 150 μm/s. The abnormal decrease in fatigue life of DD6 single crystal superalloy was attributed to micropore formation, coarsening of γ′ precipitates and recrystallization. Thus, it is essential to optimize the HIP treatments in the future development of single crystal superalloy blades.