Ablation behavior of C/SiC with YSZ and ZrB₂ coatings under high-energy laser irradiation

Carbon fiber-reinforced silicon carbide (C/SiC) composites are important candidates for laser protection materials. In this study, ablation mechanism of C/SiC coated with ZrO₂/Mo and ZrB₂–SiC/ZrO₂/Mo under laser irradiation was studied. ZrB₂–SiC multiphase ceramic and ZrO₂ ceramic were successfully coated on C/SiC composite by atmospheric plasma spraying technology with Mo as transition layer. Phase evolution and morphology of composite were investigated by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. Moreover, ablation behavior of the composite was investigated by laser confocal microscopy. Results showed that ablation mechanism of C/SiC composite was controlled by phase transformation, thermal reaction, and thermal diffusion, with solid–liquid transition of ZrB₂ and ZrO₂ being dominant factor. Endothermic reaction and good thermal diffusivity of coatings were also important factors affecting ablation performance. Reflectivity effect of ZrO₂ coating was limited under high-energy laser irradiation. Compared with ZrO₂/Mo single-phase-monolayer coating, designed ZrB₂–SiC/ZrO₂/Mo coating showed better ablation performance, and breakdown time of C/SiC increased from 10 to 40 s. The depletion of liquid phase in molten pool was identified as an important factor responsible for rapid failure of C/SiC. The coating failed when the entire liquid phase was consumed within molten pool, followed by rapid damage of C/SiC substrate. Results of this study can provide theoretical guidance and research ideas for design and application of laser protective materials.